1.FeCrAl Electrictrical Resistance Heating alloys with high electrical resistivity, temperature coefficient of resistance is small, high operating temperature. good corrosion resistance under high temperature, and particularly suitable for use in a gas containing sulfur and sulfides, low price,...

1Furnace Heating Element Wire

1.FeCrAl Electrictrical Resistance Heating alloys with high electrical resistivity, temperature coefficient of resistance is small, high operating temperature. good corrosion resistance under high temperature, and particularly suitable for use in a gas containing sulfur and sulfides, low price, it is widely used in industrial electric furnace, household appliances, far infrared device ideal heating material.

FeCrAl type:1Cr13AI4, 0Cr21AI4, 0Cr21AI6, 0Cr25AI5, 0Cr21AI6 Nb, 0Cr27AI7Mo2 etc.Series electric flat belt, electric fire wire

 

2.Nickel chromium alloy with iron resistance electrothermal high resistivity, surface body sexual well. At high temperature and high intensity, and a good performance and processing may welding nature widely used metallurgical, electrical, mechanical components and electrical manufacturing industries for doing heat resistance material. Ni-Cr Type:Cr20Ni80,Cr15Ni60, Cr20Ni35, Cr20Ni30, Cr25Ni20 etc.Series electric flat belt, electric fire wire.

Product size:

wire dia.0.05—12mm; flat strip thickness 0.03—5mm,flat strip width0.2—500mm.


Brand name

1Cr13Al4

0Cr25Al5

0Cr21Al6

0Cr23Al5

0Cr21Al4

0Cr21Al6Nb

0Cr27Al7Mo2

Main chemical composition%

Cr

12.0-15.0

23.0-26.0

19.0-22.0

22.5-24.5

18.0-21.0

21.0-23.0

26.5-27.8

Al

4.0-6.0

4.5-6.5

5.0-7.0

4.2-5.0

3.0-4.2

5.0-7.0

6.0-7.0

RE

opportune
amount

opportune
amount

opportune
amount

opportune
amount

opportune
amount

opportune
amount

opportune
amount

Fe

Rest

Rest

Rest

Rest

Rest

Rest

Rest







Nb0.5

Mo1.8-2.2

Max.continuous
service temp.of
element (ºC)

950

1250

1250

1250

1100

1350

1400

Resistivity
μΩ.m,20ºC

1.25

1.42

1.42

1.35

1.23

1.45

1.53

Density
(g/cm3 )

7.4

7.10

7.16

7.25

7.35

7.10

7.10

Thermal
conductivity
KJ/m.h.ºC

52.7

46.1

63.2

60.2

46.9

46.1

45.2

Coefficient of
lines expansion
α×10-6/ºC

15.4

16.0

14.7

15.0

13.5

16.0

16.0

Melting pointºC

1450

1500

1500

1500

1500

1510

1520

Tensile strength
Mpa

580-680

630-780

630-780

630-780

600-700

650-800

680-830

Elongation at
rupture %

>16

>12

>12

>12

>12

>12

>10

Variation of
area %

65-75

60-75

65-75

65-75

65-75

65-75

65-75

Repeat bending
frequency(F/R)

>5

>5

>5

>5

>5

>5

>5

Hardness(H.B.)

200-260

200-260

200-260

200-260

200-260

200-260

200-260

Micrographic
structure

Ferrite

Ferrite

Ferrite

Ferrite

Ferrite

Ferrite

Ferrite

Magnetic
properties

Magnetic

Magnetic

Magnetic

Magnetic

Magnetic

Magnetic

Magnetic


3Furnace Heating Wire details



Superb Heater Technology has been focused on the production of furnace heater element wire since 1985, which is well-known as one of the leading manufacturers and suppliers of furnace heater element wire. In the past years, we owned strong reputation for the high quality, reliable performance and strong durability of our products. Should you are interested, please feel free to contact our factory.

Previous: Furnace Heating Coil Furnace Resistance Wire

Next: Spiral Resistance Furnace Wires